The magnesia content of ladle magnesia carbon brick is more than 90%

Ladle magnesia carbon brick is an alkaline refractory with magnesia content of more than 90% and periclase as the main crystalline phase. Generally, it can be divided into sintered magnesia brick (also known as sintered magnesia brick) and chemically bonded magnesia brick (also known as unburned magnesia brick). Magnesia carbon brick manufacturers, magnesia bricks with high purity and firing temperature are called directly bonded magnesia bricks due to direct contact with periclase grains; Bricks made from fused magnesia are called fused reconstituted magnesia bricks. Generally, it can be divided into sintered magnesia brick (also known as sintered magnesia brick) and chemically bonded magnesia brick (also known as unburned magnesia brick). Magnesia bricks with high purity and firing temperature are called directly bonded magnesia bricks because periclase grains are in direct contact; Bricks made from fused magnesia are called fused reconstituted magnesia bricks. Magnesia brick

Converter magnesia carbon brick has high fire resistance, good alkali slag resistance, high load softening starting temperature, but poor thermal shock resistance. Sintered magnesia brick is made of magnesia brick. After crushing, batching, mixing and forming, it is fired at a high temperature of 1550 ~ 1600 ℃, and the firing temperature of high-purity products is more than 1750 ℃. Non pouring magnesia brick is made by adding appropriate chemical binder into magnesia, mixing, forming and drying. Based on the experience of producing magnesia bricks, the magnesia brick company aims to make the kiln lining materials give full play to their efficiency and ensure the service cycle of kiln lining materials